Welding Machine Rods and Wires

tig160 dc inverted argon arc welding machine n Welding Machine Rods and Wires


Bare welding wires and rods are used in short lengths of about 1 meter or in coiled form in spools. Whereas short lengths are used for processes like tig welding machine and plasma arc welding machine wherein they are not part of the welding circuit, long wires are employed for processes like mig welding machine and saw welding machine where a part of the wire conducts current. When a welding wire forms a part of the electrical circuit is called a welding electrode otherwise it is referred to as a welding rod.

Most wires used for welding structural steel usually contain 0.10% carbon and 0.35 to 0.60% manganese content. Some other types have increased amounts of carbon, manganese and silicon.

Excess silicon in welding wire results in heavy spatter, gassing in the weld pool, and non-metallic materials in the weld metal. Maximum silicon content permitted, therefore, is upto 0.95%.

The contents of harmful impurities like sulphur and phosphorous should not exceed 0.04% each. In some wires, particularly those used for welding alloy steels the maximum amount of sulphur and phosphorous allowed is each 0.03% each.

The range of wire diameter extends from 0.5 to 2.5 mm with 0.5, 0.6, 0.8, 0.9, 1.0, 1.2, 1.6, 2.0, 2.4 and 2.5 mm diameter wires being normally available. Welding machines use continuous wires in coils. Depending on the wire diameter, a coil may weigh anywhere between 5 to 500 Kg and measure 150 to 1000 mm across.

The welding wires are usually copper coated to prevent rusting and to improve current pickup from the contact tube, it also helps during drawing of wires through dies. To avoid harmful effects and peeling of copper coating it is usually kept very thin and the maximum amount of copper is specified at 0.4% by weight of the wire.

Apart from low carbon steels, welding wires are also produced from stainless steels, aluminum and its alloys, nickel alloys, magnesium alloys, titanium alloys, and copper alloys.

The welding wires are available both in solid and tubular forms, the latter contains flux in it.

Specifications for Solid Wires and Rods

Several systems are in use to specify welding electrodes and rods. AWS specification is one of the well known systems of codification. It consists of a prefix letter or letter S and then a suffix which may be figure or a letter or both.

Prefix Letter Indication
E a welding electrode
R a welding rod
RB a welding rod/brazing filler
ER an electrode or a welding rod

Methods of Arc Initiation for Welding Machines

It is not possible to create an arc between the electrode and the work piece just by connecting them in a welding circuit. This is because the current needs an ionized passage for flowing across the gap. Thus, a welding arc needs to be initiated. The method of initiating a welding arc depends upon the process used. However, in general these methods can be grouped into two categories. In one category the ionization of the gases between the electrodes to work gap achieved by the application of high voltage across it and in the other category the electrode and the work piece are short-circuited momentarily by touching each other. The former is used for immobile or fixed arcs and the latter for mobile or traveling arcs.

For immobile arcs the electrode and work piece are bought close to each other without touching and a high voltage of the order of 104 volts is applied. As a high voltage at normal mains frequency of 50 hertz will be lethal thus high frequency high voltage is applied, for arc initiation, with the help of the spark gap oscillator. Thus helps in ionizing the gases in the gap between the electrode and the work piece and the arc are, thus initiated in a few milli-seconds. As soon as the arc is stabilized, the auxiliary high frequency high voltage supply is switched off automatically. This method of arc initiation is utilized in the gas tungsten arc welding machine and carbon arc welding machine processes so as to avoid the contamination of tungsten electrode or to eliminate the chance of pickup of carbon from the carbon electrode if touch method is used to initiate the arc.

The touch method of initiating the arc is normally used for processes in which the mobile arc is employed. However, it has two variants depending upon the size i.e. diameter of the electrode. For thick electrodes, the arc initiation is done by touching the electrode to the work piece and then withdrawing it. Upon touching, a heavy short circuit current flows in the circuit causing melting of minute points of contact. When the electrode is withdrawn it results in sparking and ionization of the gap between the electrode and the work piece. If the arc is not initiated at the first attempt, the process is can be repeated till a stable arc is established. This method of initiating the welding arc is known as ‘touch’ method and the arc so initiated is called ‘drawn’ arc. The method is used for arc initiation in arc welding machine process or SMAW process.

For welding with wires i.e. thin electrodes an electrode is fed to the work at a pre-set rate. As soon as it touches the work piece, heavy short circuit current flows through it and the electrode melts resulting in ionization is adopted for gas metal arc welding or MIG welding machine and SAW welding machine and their processes, both in the semi-automatic and automatic modes.

In some limited cases the welding arc is also initiated by placing a ball of steel wool between the electrode and the work piece. When a heavy current flows through steel wool it melts and in the process provides an ionized and metal vapour path for the flow of current and a stable arc is established.

Welding Machine- D.C. Welding Power Sources

This type of welding power source usually consists a transformer and a bank of rectifying cells. A unit rectifying cell is called a diode and it allows the electrical current to pass only in one direction and thus helps in converting alternating current to direct current.

The welding industry uses solid-state devices like semi-conductors to make rectifying cells. Earlier selenium was mainly used to make these cells but because of the demand for higher economy, reliability, and efficiency most rectifying cells are now made of silicon.

In comparison with motor-generator welding set, a rectifier welding power source has the following advantages.


  • No rotating parts, easy maintenance,
  • Higher efficiency,
  • Smaller weight, size and cost.


General theory of DC Rectifier Design

Due to easy control of heat balance as well as the ease of arc initiation and its maintenance, dc is used particularly for bare wire welding like mig welding machine. However, ac is more easily and commonly available. The best solution, therefore, appears to be to use ac to produce the required dc and that is done with the help of a dc generator, a convertor or a dc rectifier.

Basically an electric rectifier is a device which permits flow of current on one direction only and can thus convert ac into a fluctuating dc. In the case of sinusoidal supply voltage suppression of the negative half of the curve results in intermittent pulses of energy which show no reversal in polarity. Obviously, such a source of supply would not be suitable for welding as periods of interrupted supply of energy between consecutive pulses would make it impossible to maintain a stable arc.

This difficulty can, however, be overcome if the source of supply is a three-phase current, each phase displaced by 1200 with reference to preceding or succeeding phases. When the negative half cycles of all three phases are suppressed the resulting graph for the uni-directional current shows an approach to straight line with much smaller fluctuations than that in the case of single phase. On similar basis, systems with more than three phase ac would attain better closeness to true dc transient. However, it is common to come across systems with more than three phases, thus three phase system is the one most used. But there is another way of improving the shape of the rectified current, and that is referred to as full-wave rectification.

DC rectifier, as mentioned earlier, is a device which permits current flow in one direction only, or more correctly it suppresses most of the current flow in reverse direction. Although the relation between voltage and current in the first quadrant of the graph is not linear, it can be noticed that for the third quadrant even a very large increase in voltage results in transmission of very small amount of current.

As is evident from the different transients of rectified current, there is inherent fluctuation in such a system. One method of obtaining smooth dc from a rectifier unit is the use of capacitors. If a capacitor is connected in the circuit it stores energy and supplies the same at nearly constant output voltage, although the energy received by it from the rectifier is in variable pulses.

Initially mercury arc rectifiers were developed but they are very fragile and have now been completely replaced by solid-state rectifiers.

Voltage-Current Characteristics of Welding Machine

V-I Characteristics of Welding Machine


welding machine new Voltage Current Characteristics of Welding Machine


Means for different welding plant different V-I characteristics. It shows the relationship between the arc voltage and arc current. During the welding arc length between the electrode tip and the workpiece determines the arc resistance and consequently the potential drop across the arc. In other manner, the arc length find out the arc voltage longer the arc length higher the arc voltage and it is this voltage which allow certain flow of current according of the characteristics of welding plant (unit).


There are basically three type of characteristics:

  1. Drooping characteristics (or constant current)
  2. Flat (or constant voltage)
  3. Rising voltage type

Our all concentration will be on only drooping type characteristics as it is used mostly in arc welding machine plant, both ac and dc type.


1.       Drooping Type (Constant Current): Drooping V-I characteristics is used on constant current type welding machine. When arc is struck in arc welding machine (GMAW Welding Machine) electrode is essentially in short-circuit which would immediately required a sudden of current otherwise machine is design to prevent this. A constant current machine is design to minimise theses sudden surges.

As we know that a manual metal arc welding plant consist a drooping V-I characteristics. Drooping means that the terminal voltage of welding machine decreases as the welding current increases. In arc welding machine (MMA Welding) , arc length (gap between the workpiece and electrode) length, from a shorter arc B to longer arc A, there is a marked variation(K) in the voltage but the corresponding variation (c) in the current is very small.

Drooping V-I characteristic is applicable for both AC and DC welding machine which is used for SMAW Welding Machine, TIG Welding Machine, and Submerged Arc Welding Machine (SAW Welding Machine) and Plasma Arc Welding Machine and the MMA (Manual Metal Arc) Welding Machine, voltage at the time of welding is approximate 30-40 V.


2.       Flat or constant voltage type characteristics are used with semi-automatic MIG Welding Machine and other automatic welding machines.


3.       Rising voltage type characteristics are used with fully automatic welding machine.

a)      Open circuit voltage usually is in the range of 70 to 80 volt.

b)      System to adjust welding current is usually in the AC section of the machine before the rectifiers control of current   is based on the principle of variable inductance or impedance various method for varying impedance for current control are as:


a) Moving shunt

b) Tapped reactor

c) Moving coil

d) Saturable reactor

e) Moving reactor core


In welding circuit flow of current is controlled by inductor in line between the electrode and transformer current can be vary by varying the inductance. For current control during welding a means of varying this inductance is must.


a) Tapped type reactor

b) Moving core type reactor

c) Saturable type reactor

Flux Cored Arc Welding Machine (FCAW Welding Machine)

INMIG 400AMP Flux Cored Arc Welding Machine (FCAW Welding Machine)

This process is growing in popularity. It is being used for more than 20% of arc welding machine. Some FCAW still uses CO2 shielding, but the use of flux cored wire alone is increasing. In many cases, the flux-cored wire alone produces welds equal to or better than the original metal and its uses eliminates the need for the gas shield equipment and cost of the gas.


Definition and Concept

The FCAW is a process in which coalescence is produced by heating with an electric arc between a continuous tubular consumable electrode and the work. The electrode is flux cored, i.e. the flux is contained within the electrode which is hollow. In addition to flux, mineral and ferro alloys in the core can provide additional protection and composition control.

The flux cored electrode is coiled and supplied to the arc as a continuous wire as in CO2 welding. The flux inside the wire provides the necessary shielding of the weld pool. Additional shielding may (or may not) be obtained from an externally supplied gas (e.g. CO2) or gas mixture.

Principle of Operation

As explained above, FCAW utilizes the heat of an arc between continuously fed consumable flux cored electrode and the work. The heat of the arc melts the surface of the base metal and the end of the electrode. The metal melted off the electrode is transferred through the arc to the workpiece where it becomes the deposited weld metal. Shielding is obtained from the disintegration of ingredients contained within the flux cored electrode. Additional shielding may be obtained from an envelope of gas supplied through a nozzle to the arc area. Ingredients within the electrode produce gas for shielding and also provide deoxidizers, ionizers, purifying agents and in some cases alloying elements (for composition control). These ingredients from a glasslike slag, which is lighter in weight than the deposited weld metal and which floats on the surface of the weld as a protective cover. The flux cored electrode is fed into the arc automatically from a coil. The arc is maintained automatically and arc travel can be manual or by machine.

Butt Welding Machine

butt welding machine Butt Welding MachineThe ends to be welded touch each other before the current is switched on. A heavy current is then passed from one piece to another and the contacting faces are heated up due to the contact resistance. The two pieces are pressed together firmly after the desired welding temperature of 870 to 925 oC is reached. The pressing action which results in the increase in lateral dimension of the workpieces is called upsetting. Upsetting takes place both during and after the current flow. The upsetting action results in welding of end faces with squeezing of a part of the softened metal to form a fin, which can be removed later, if required, by machining.

Resistance butt welding is used for end joining of rods, tubes, bars and similar other sections. However, an important application of this process is the large scale production of tubes and pipes at a high rate of production and the process is then referred to as resistance butt-seam welding or simply as electric resistance welding (ERW). In ERW process, the strip for tube making is continuously edge shared and rolled into tube for forming a longitudinal seam.

Current of upto 40,000 amperes at 5 volt is introduced across the joint by split electrode rollers and the force is applied by the pressure rolls. In this process, both the work motion and current and supply are continuous. The flow of current through the shunt path is avoided or reduced by the use of ferrite or wrought iron ‘impeder’ placed inside the tube.

The maximum speed of production is controlled by the frequency of the current as that decides the number of zero-current periods per unit time. Frequencies upto 350 Hz are commonly used which results in the production rate of about 36 m/min. The fin formed due to extruded metal is continuously removed by cutters and the desired length of the tube or pipe is cut on the production table without any interruption in the process of welding.

Stud Welding

stud welding equipment Stud WeldingThis is a process of welding stud (a headless threaded bolt) or stud-like pieces (e.g. bolts, screws, rivets, rods, etc.) to flat workpieces like plates. Its a unique process which combines arc and forge welding processes and results in tremendous cost saving when compared to the conventional methods like drilling and tapping.

Stud welding was first used by British Navy in 1918 but its regular and extensive use started from 1938. There are four variations of the process viz., capacitor discharge stud welding, the drawn arc capacitor discharge stud welding, the consumable ferrule stud welding and the drawn arc stud welding. The last variation of the process is the most popular and the following description pertains to that only.

The main equipment for stud welding consists of a stud welding gun, a time control unit, a dc power source of 300 to 600 amperes current capacity, studs, and ceramic ferrules.

A stud is held in the welding gun and a ferrule is slipped on it. The stud is then made to touch the cleaned spot (shot blasted, ground, or wire brushed) where it is to be welded and the switch in the form of gun trigger is pressed and the process is completed in a couple of seconds. This necessitates the use of ultra-high speed power source to supply the desired welding current. A stud about 40 mm diameter requires about 5000 ampere current at 65 to 70 volts for 2 seconds. Therefore, motor-generator sets with their higher overload capacities are preferred over the rectifier welding sets.

For efficient results the plate on which the stud is to be welded must have the minimum thickness at least 20% that of the diameter of the stud, however for developing full strength it should not be less than 50% of the diameter of the stud base.

Current and Power Source Rating for Different Stud Sizes

Stud Diameter (mm) Current Required (amp) Power Rating (amp) Source Number
5 325 300 1
8 500 400 1
10 625 600 1
13 925 1000 1
15 1100 1000 1
19 1600 1000 2
22 1750 1000 2
25 2000 1000 2

Stud welding is used mainly for mild steel, low alloy steels, and austenitic stainless steels. Drawn arc stud welding is not used for non-ferrous metals but other variants of the process can be utilized for welding lead free brass, bronze, chrome plated metals and aluminum. However heat-treatable aluminum alloys are not recommended for stud welding.

Typical applications of stud welding include steel decks of ships, for attaching brackets, hangers, cover plates, conduits, piping, etc. to metal workpieces. The process also finds wide use in automotive rail road machinery manufacturing and construction industries.

Spot Welding Machine

6 4f5ebcfb88018 Spot Welding Machine



Spot Welding Process

All resistance welding operations are automatic and therefore all process variables are pre-set and maintained constant. Once a welding operation has been initiated there is no way in which its progress can be controlled and, thus, the weld cycle is completed as per the pre-set times.


Welding Cycle

The welding cycle for spot welding machine, seam welding machine and projection welding machine consist basically of four elements viz., squeeze time, weld time, hold time, and off time. These timing are pre-set for a particular metal and a thickness range and the shop operator normally cannot change them on his own. Each one of these four time phases has its own role to play in achieving a sound weld of the required size.


Squeeze Time

The time interval between the application of electrode pressure to the work and switching on the welding currents called the squeeze time. This time interval is provided to assure the contact between the electrode and the work and to initiate the application of force on it.


Weld Time

It is the time for which the welding current actually flows to melt the metal at the interface.


Hold Time

It is the time for which the electrodes are kept in position, after the welding current is switched off, to assure the application of pressure so as to consolidate the molten metal into a nugget which is then cooled by the dissipation of heat to the surrounding work material. If the applied force is excessive it may result in expulsion of molten metal from in-between the sheets.


Off Time

The time allowed to shift the work to the next location before the cycle is repeated is referred to as the off time. The electrodes are kept off the work during this time interval.


Welding Variables

Welding current, time of current flow and the electrode pressure are recognized as the fundamental variables of resistance spot welding machine. For achieving quality welds in most metals, these variables are required to be kept within very close limit.


Welding Current

The size of the weld nugget and in fact whether it will form or not depends upon the heat being generated faster than it is dissipated by conduction. Welding current is, thus , the most critical variable.

Both a.c. and d.c. are used to produce spot, seam, and projection welding machine. Most applications use single phase a.c. of mains frequency i.e. 50 hertz. However, d.c. is used for applications that need heavy current and the load for which can be balanced on a 3-phase power line. Also, with direct current machines the rate of current rise and fall can be programmed as per requirements. The current rise period or upslope and current decay period or down slope can be programmed with electronic control systems.

Control of upslope helps to avoid overheating and expulsion of molten metal at the beginning of the weld time as the interface resistance at that time is high. Down slope helps to control weld nugget solidification to avoid cracks in weldments particularly in metals that are prone to quench-hardening and hot tearing.


MIG Welding Machine

mig 350i inverter co2 gas shielded welding machine  MIG Welding MachineIntroduction:

MIG Welding machine is defined as metal inert gas welding. It is also one of the types of arc welding machine. In this process no pressure is applied for welding. In this process of welding wherein coalescence is produced by heat the work piece with an electric arc establish between a  continues feed of metal electrode (copper coated) and the work piece. No flux is used as used in submerged arc welding (SAW Welding) but a shielding gas (Ar, He, Co2) is used. It is also known as gas metal arc welding (GMAW).

Principle of Operation

Before welding set the current, wire feed speed and electrical connections. Now arc is struck by one of the two methods.

1st method current and shielding gas flow is switched on and electrode is scratched against the job as usual practice.

For striking the arc by 2nd method-electrode is made to touch the job is restricted and moved forward to carry out welding but before striking the arc shielding gas, water and current is switched on during the welding. Torch should be 10 – 12 mm. Away from the work pieces and arc length is kept between 1.5 to 4.0 mm. Arc are basically two types.

I.            Self adjusted arc

II.          Self controlled arc

In self adjusted arc, with decreases in arc length (from L2 to L1) voltage decreases and current increases from l2 to l1 melting the electrode at faster rate resulting into making the arc length normal for self adjusting arc, welding source with flat characteristics is required for self-controlled arc, when arc length decreases, arc voltage also decreases with reduces speed of electric motor and hence the feed rate of electrode this brings arc length to a set value for self-controlled arc, a welding source with dropping characteristics is preferred.


Equipment Required for MIG Welding Machine

I.             Welding power source with cables;

II.           Welding gun filler wire on a coiled spool;

III.         Shielding gas cylinder, pressure regulator and flow meter;

IV.          Control switch.


Different Types of Material can be welded by MIG Welding Machine

I.            Carbon and low alloy steel

II.          Heat resistant alloys

III.        Copper and its alloys

IV.         High strength low alloy steel (HSLA)

V.           Stainless Steel

VI.         Magnesium alloys

VII.       Aluminum and its alloys


Advantage of MIG Welding Machine

I.            Less number of spatters as compared with MMA welding;

II.           MIG is very faster process as compared with TIG Welding Machine;

III.         Deep penetration can be achieved through this process;

IV.          No use of flux during welding process;

V.            Process can be easily mechanized;

VI.          MIG produces a high quality, weld bead with minimum defeats;

VII.        Large metal deposition rate are achieved by MIG welding process.


Limitations of MIG Welding Machine

I.            Welding equipment is more costly and complex as compared to ARC Welding Machine;

II.          Trained operator is required to perform the operation;

III.         Process is not economically for job shop production;

IV.         All types of material cannot be welded.



I.             For welding of Al, Cu, Mg, Ni and their alloys;

II.           For welding of aircraft, pressure vessels and shipbuilding industry;

III.         For manufacturing of refrigerator parts etc;

IV.          Rail road industries;

V.            Transport Industries.


DSC02057 Copy ARC WELDING MACHINE AND PROCESSArc Welding is a welding process where in coalescence is produced by heating with an electric arc. Mostly arc welding is done by without pressure and with or without use of filler metal depending upon the plate (object) thickness.

In arc welding machine arc is formed when an electric current passes between two electrodes separated by a short distance from each other. In arc welding machine one electrode is the welding rod or wire while other is the metal to be welded (work piece), electrode and plate. Arc connected to the supply one of the positive pole and other to negative terminal. Arc is started by moment rally touching the electrode on the plate and the withdrawing it to about 3 to 4 mm from the plate. When the electrode touches the plates, a current flows and as it is withdrawn from the plate the current continues to flow in the form of a spark across the very small gap first formed, this cause the air gap to become ionized or made conducting and as a result the current is able to flow across the gap even when it is very wide, in the form of an electrode must always be touched on to the plate before the arc can be started.

Arc is generated be electrons flowing from negative (-ve) to positive (+ve) terminal and electrical energy is changed in the arc into heat and light approximately 2/3 of the heat is generated near the positive (+ve) terminal which burns into the form of a creater. Temperature range from 2700oC-5500oC. While remaining 1/3 is generated near negative (-ve) terminal as electrode connected with positive (+ve) terminal they will burn away 50% faster than if connected to negative (-ve) terminal. Therefore medium coated electrodes and bare electrodes are used.

Types of Arc Welding Machines

1.       Consumable Electrode Process

i.            Shielded Metal Arc Welding (SMAW) or Arc Welding Machine

ii.            SAW Welding Machine

iii.            MIG Welding Machine

iv.            FCAW Welding Machine

v.            Electrogas Welding (ECW)

vi.            Electroslag Welding (ESW)

vii.            Carbon Arc Welding (CAW)

 2.       Non-consumable Electrode Processes

i.            TIG Welding Machine

ii.            Atomic Hydrogen Welding (AHW)

iii.            Plasma Arc  Welding (PAW)